China OEM Film Packaging Companies - Low Melt FFS Packaging Film – Zonpak
China OEM Film Packaging Companies - Low Melt FFS Packaging Film – Zonpak Detail:
Low melt FFS packaging film is specially designed for the packaging of rubber chemicals on a form-fill-seal machine. The best feature of the film is its low melting point and good compatibility with natural and synthetic rubber. The bags made with the film on FFS machine can be direct put into an internal mixer during rubber or plastic mixing process. The bags can easily melt and fully disperse into the rubber compounds as a minor ingredient.
The film has stable chemical properties, can fit most rubber chemicals. Good physical strength makes the film suit most automatic FFS packing machines. Films with different melting points and thickness are available for different using conditions.
|
Technical Standards |
|
| Melting point | 65-110 deg. C |
| Physical properties | |
| Tensile strength | MD ≥16MPa TD ≥16MPa |
| Elongation at break | MD ≥400% TD ≥400% |
| Modulus at 100% elongation | MD ≥6MPa TD ≥3MPa |
| Appearance | |
| Surface of the product is flat and smooth, there is no wrinkle, no bubble. | |
Product detail pictures:
Related Product Guide:
"Sincerity, Innovation, Rigorousness, and Efficiency" may be the persistent conception of our organization to the long-term to build together with shoppers for mutual reciprocity and mutual advantage for China OEM Film Packaging Companies - Low Melt FFS Packaging Film – Zonpak, The product will supply to all over the world, such as: kazakhstan , Danish , Senegal , Our company has already had a lot of top factories and qualified technology teams in China, offering the best goods, techniques and services to worldwide customers. Honesty is our principle, skilled operation is our work, service is our goal, and customers' satisfaction is our future!
By Julie
from Netherlands
- 2017.04.08 14:55
A good manufacturers, we have cooperated twice, good quality and good service attitude.
By Dee Lopez
from Swiss
- 2018.09.29 17:23