Good Quality Low Melt EVA Film - EVA Batch Inclusion Film – Zonpak
Good Quality Low Melt EVA Film - EVA Batch Inclusion Film – Zonpak Detail:
ZonpakTM EVA batch inclusion film is a special kind of packaging film with specific low melting point. It is mainly used on the automatic FFS (form-fill-seal) packing machine to make little packages (100g-5000g) of rubber additives or chemicals. Due to the film’s property of low melting point and good compatibility with rubber and plastic, these little packages can be direct put into an internal mixer during mixing process, and the bags will melt and fully disperse into the mix as an effective ingredient. It brings convenience to the material users and eliminates packaging waste disposal.
Different melting points are available as customers required. Stable chemical properties and high physical strength of the film make it suitable for most rubber chemicals and automatic packaging machines.
|
Technical Standards |
|
| Melting point | 65-110 deg. C |
| Physical properties | |
| Tensile strength | MD ≥16MPa TD ≥16MPa |
| Elongation at break | MD ≥400% TD ≥400% |
| Modulus at 100% elongation | MD ≥6MPa TD ≥3MPa |
| Appearance | |
| Surface of the product is flat and smooth, there is no wrinkle, no bubble. | |
Product detail pictures:
Related Product Guide:
Sticking to the principle of "Super Quality, Satisfactory service" ,We are striving to be a good business partner of you for Good Quality Low Melt EVA Film - EVA Batch Inclusion Film – Zonpak, The product will supply to all over the world, such as: Miami , Poland , Colombia , We adopted technique and quality system management, based on "customer orientated, reputation first, mutual benefit, develop with joint efforts", welcome friends to communicate and cooperate from all over the world.
By Anastasia
from Germany
- 2018.10.01 14:14
This is a honest and trustworthy company, technology and equipment are very advanced and the prodduct is very adequate, there is no worry in the suppliment.
By Karl
from Saudi Arabia
- 2017.08.16 13:39