High Quality Low Melt FFS Film - Low Melt FFS Packaging Film – Zonpak
High Quality Low Melt FFS Film - Low Melt FFS Packaging Film – Zonpak Detail:
Low melt FFS packaging film is specially designed for the packaging of rubber chemicals on a form-fill-seal machine. The best feature of the film is its low melting point and good compatibility with natural and synthetic rubber. The bags made with the film on FFS machine can be direct put into an internal mixer during rubber or plastic mixing process. The bags can easily melt and fully disperse into the rubber compounds as a minor ingredient.
The film has stable chemical properties, can fit most rubber chemicals. Good physical strength makes the film suit most automatic FFS packing machines. Films with different melting points and thickness are available for different using conditions.
|
Technical Standards |
|
| Melting point | 65-110 deg. C |
| Physical properties | |
| Tensile strength | MD ≥16MPa TD ≥16MPa |
| Elongation at break | MD ≥400% TD ≥400% |
| Modulus at 100% elongation | MD ≥6MPa TD ≥3MPa |
| Appearance | |
| Surface of the product is flat and smooth, there is no wrinkle, no bubble. | |
Product detail pictures:
Related Product Guide:
we could supply good quality goods, aggressive cost and very best purchaser assistance. Our destination is "You come here with difficulty and we supply you with a smile to take away" for High Quality Low Melt FFS Film - Low Melt FFS Packaging Film – Zonpak, The product will supply to all over the world, such as: Macedonia , Netherlands , Holland , We are in continuous service to our growing local and international clients. We aim to be worldwide leader in this industry and with this mind; it is our great pleasure to serve and bringing the highest satisfaction rates among the growing market.
By Mignon
from Grenada
- 2018.04.25 16:46
This enterprise in the industry is strong and competitive, advancing with the times and develop sustainable, we are very pleased to have a opportunity to cooperate!
By Ella
from Belgium
- 2018.07.27 12:26