OEM China Film Packaging Material - Low Melt FFS Packaging Film – Zonpak
OEM China Film Packaging Material - Low Melt FFS Packaging Film – Zonpak Detail:
Low melt FFS packaging film is specially designed for the packaging of rubber chemicals on a form-fill-seal machine. The best feature of the film is its low melting point and good compatibility with natural and synthetic rubber. The bags made with the film on FFS machine can be direct put into an internal mixer during rubber or plastic mixing process. The bags can easily melt and fully disperse into the rubber compounds as a minor ingredient.
The film has stable chemical properties, can fit most rubber chemicals. Good physical strength makes the film suit most automatic FFS packing machines. Films with different melting points and thickness are available for different using conditions.
Technical Standards |
|
Melting point | 65-110 deg. C |
Physical properties | |
Tensile strength | MD ≥16MPa TD ≥16MPa |
Elongation at break | MD ≥400% TD ≥400% |
Modulus at 100% elongation | MD ≥6MPa TD ≥3MPa |
Appearance | |
Surface of the product is flat and smooth, there is no wrinkle, no bubble. |
Product detail pictures:
Related Product Guide:
Our corporation insists all along the quality policy of "product top quality is base of organization survival; purchaser pleasure will be the staring point and ending of an company; persistent improvement is eternal pursuit of staff" plus the consistent purpose of "reputation very first, purchaser first" for OEM China Film Packaging Material - Low Melt FFS Packaging Film – Zonpak, The product will supply to all over the world, such as: Saudi Arabia , Nigeria , Italy , Our production have been exported to more than 30 countries and regions as first hand source with lowest price. We sincerely welcome customers from both at home and abroad to come to negotiate business with us.
By Kelly from Swaziland - 2018.12.10 19:03
Superb technology, perfect after-sales service and efficient work efficiency, we think this is our best choice.
By Lulu from Leicester - 2018.07.12 12:19