Reasonable price EVA Film - EVA Film for Automatic FFS Packaging – Zonpak
Reasonable price EVA Film - EVA Film for Automatic FFS Packaging – Zonpak Detail:
ZonpakTM EVA film is specially designed for automatic form-fill-seal (FFS) packaging of rubber chemicals. Manufacturers of rubber chemicals can use the film and FFS machines to make 100g-5000g uniform packages for rubber compounding or mixing plants. These little packages can be direct put into an internal mixer during the mixing process. The bags made of the film can easily melt and fully disperse into the rubber as an effective ingredient. It brings convenience to material users and helps raise production efficiency while decrease the cost and material waste.
Films with different melting points are available for different application. Thickness and width of the film can be custom made as customer required.
Technical Standards |
|
Melting point | 65-110 deg. C |
Physical properties | |
Tensile strength | MD ≥16MPa TD ≥16MPa |
Elongation at break | MD ≥400% TD ≥400% |
Modulus at 100% elongation | MD ≥6MPa TD ≥3MPa |
Appearance | |
Surface of the product is flat and smooth, there is no wrinkle, no bubble. |
Product detail pictures:
Related Product Guide:
Fast and good quotations, informed advisers to help you choose the correct product that suits all your needs, a short production time, responsible quality control and different services for paying and shipping affairs for Reasonable price EVA Film - EVA Film for Automatic FFS Packaging – Zonpak, The product will supply to all over the world, such as: Naples , Mongolia , Algeria , We always insist on the principle of "Quality and service are the life of the product". Till now, our products have been exported to more than 20 countries under our strict quality control and high level service.
By John biddlestone from Malawi - 2017.06.19 13:51
High production efficiency and good product quality, fast delivery and completed after-sale protection, a right choice, a best choice.
By Michaelia from Turkmenistan - 2017.08.18 18:38